• Source: Delay composition

Delay composition, also called delay charge or delay train, is a pyrotechnic composition, a sort of pyrotechnic initiator, a mixture of oxidizer and fuel that burns in a slow, constant rate that should not be significantly dependent on temperature and pressure. Delay compositions are used to introduce a delay into the firing train, e.g. to properly sequence firing of fireworks, to delay firing of ejection charges in e.g. model rockets, or to introduce a few seconds of time between triggering a hand grenade and its explosion. Typical delay times range between several milliseconds and several seconds.
A popular delay charge is a tube of pressed black powder. The mechanical assembly prevents the outright detonation of the charge.
While delay compositions are principally similar to other fuel-oxidizer compositions, larger grain sizes and less aggressively reacting chemicals are used. Many of the compositions generate little or no gas during burning. Typical materials used are:

Fuels: silicon, boron, manganese, tungsten, antimony, antimony trisulfide, zirconium, zirconium–nickel alloy, zinc, magnesium, etc.
Oxidizers: lead dioxide, iron oxides, barium chromate, lead chromate, tin(IV) oxide, bismuth(III) oxide, barium sulfate (for high-temperature compositions), potassium perchlorate (usually used in small amount together with other oxidizers), etc.
Additives to cool down the flame and slow down the reaction can be employed; inert materials or coolants like titanium dioxide, ground glass, chalk, sodium bicarbonate, etc. are common.
The burn rates are dependent on: [1]

nature of fuel - fuels that release more heat burn faster
nature of oxidizer - oxidizers that require less heat to decompose burn faster
the composition ratio - stoichiometric mixtures burn the fastest, also slight excess of metallic fuel also increases burn rate, probably due to heat transfer
particle sizes - smaller particles burn faster, but too small particles may lead to incomplete or interrupted burn due to too narrow heating zone
mechanical assembly and housing - charge diameter and thermal conductivity of housing influence lateral heat losses
ambient temperature - ideally this dependence is very low but extremely low or extremely high temperatures may have influence
Examples of some compositions are: [2]

black powder with addition of inert material, e.g. chalk or sodium bicarbonate
lead(II) oxide with silicon, burning at 1.5–2 cm/s
red lead with silicon, burning at intermediate rate
lead(IV) oxide with silicon, burning at 5–6 cm/s
potassium permanganate with antimony, very slow
Manganese Delay Composition: manganese with lead chromate and barium chromate (lead chromate is the principal oxidizer, barium chromate acts as burning rate modifier, the more of it the slower the reaction) [3]
Tungsten Delay Composition: tungsten with barium chromate and potassium perchlorate [4]
Zirconium Nickel Alloy Delay Composition: zirconium-nickel alloy with barium chromate and potassium perchlorate.
boron with barium chromate [5]




References

Kata Kunci Pencarian:

• RMS Titanic
• Pemrosesan ulang nuklir
• 105×617mmR
• NATO 120x570mm
• Delay composition
• Pyrotechnic composition
• Roman candle (firework)
• Vladislav Delay
• Ejection charge
• Delayed coker
• Shear pin
• Composition doll
• Children (composition)
• Pyrotechnic heat source